December 14, "China Metallurgical News" reporter saw the third cold rolling mill in Beigang plate, the plant for the Beiqi New Energy Automobile Company produced another batch of tensile strength of 2,000 MPa high strength and toughness hot stamping Steel smoothly offline. Benxi Iron and Steel 2000 megabytes super-high-strength steel to achieve the world's first.

It is understood that the steel by the steel and Northeastern University jointly developed. In March this year, 2000 MPa hot stamping steel successfully off the assembly line; in June, the product batch applied to new models of Beiqi new energy vehicles; September, the successful mass production of the product, creating the year of research and development, then the application, A new record of mass production. The steel by the United States General Motors Research Institute of China and the user on-site testing, the tensile strength of 2,000 MPa, the elongation rate of 7% or more, three-point bending angle of 60 degrees, is the world's highest grade hot stamping formed steel .

Hot stamping of 2000 MPa hot-forming steel with the current 1,500 MPa grade steel grades compared to 10% to 15% weight loss. This will enable auto companies to significantly reduce production costs and bring considerable economic benefits. please contact katalor if you have need for more information about steel